UTP 485
UTP 48 contains 12% Si for welding aluminum alloys containing copper, silicon, and magnesium. It is also excellent for joining dissimilar grades of aluminum. Features a unique self-lifting slag. Its pure white coating outperforms conventional products in moisture resistance. Available in hermetically sealed aluminum tins.
| Standards: | EN ISO 18273 – E Al 4047 (AlSi12) | ||||||||||||
| Composition of the Base Metal, % (Typical) | Ni | Mon | Ti | Fe | Cu | Al | Mg | Zn | Feature | Zr | V | Be | Other |
| 11,8 | 0,04 | 6.0–8.5 | 0,8 | 0,23 | balance | 0,04 | 0,08 | ||||||
| Mechanical Specifications: | Yield Strength (MPa) | 80 | |||||||||||
| Tensile Strength (MPa) | 180 | ||||||||||||
| Percentage Elongation, A5, (%) | 5 | ||||||||||||
| Çentik Darbe Dayanımı (j/cm2 ) |
|||||||||||||
Related products
Union AlSi 10 Cu 4
Solid wire for GMAW of AlCu alloys. Provides higher strength and better ductility than AlSi filler alloys when welding AlCu alloys. Superior resistance to stress corrosion cracking in applications requiring high-temperature properties. Thorough cleaning of the workpiece bevels is necessary prior to welding.
Union AlMg 3
Solid wire for GMAW of AlCu alloys. Low melting point and excellent penetration characteristics. Provides superior wetting characteristics compared to Union AlCu 6 Mn when welding AlCu alloys; however, its strength is lower. Superior resistance to stress corrosion cracking in applications requiring high-temperature properties. The weld metal is not suitable for anodizing for decorative purposes. Thorough cleaning of the workpiece bevels is necessary prior to welding.
Union AlMg 3
Rod for GTAW of AlMg alloys containing up to 5% Mg. Seawater-resistant weld metal. Susceptible to stress corrosion cracking if exposed to service temperatures >65°C. Good colour matching with base metal after anodizing. The welding consumable contains Ti for grain refinery. Thorough cleaning of the workpiece bevels is necessary prior to welding.
Union AlSi 10 Cu 4
UTP 485 is an aluminum stick electrode containing 5% Si and featuring a special coating. It is suitable for joining and surfacing AlSi alloys with a silicon content of up to 7% and for dissimilar joints between different aluminum alloys, such as:
3.3206 AlMgSi 0.5 - 3.2371 G-AlSi 7 Mg
3.3210 AlMgSi 0.7 - 3.2341 G-AlSi 5 Mg
3.2315 AlMgSi 1 - 3.2151 G-AlSi 6 Cu 4
3.3211 AlMg 1 SiCu
UTP 485 is suitable for welding plates of wall thicknesses> 2 mm. The soft arc produces a fl at, fi newly-rippled weld seam. Easy slag removal.