Akma dayanımı 420 MPa (60 ksi)’ye kadar olan çelikler:
S235JR–E335, S235J2G3–S355J2G3, C22, C35,
P235T1–P355T1, P235T2, P355T2,
L210–L360NB, L290MB–L32MB,
P235G1TH, P255G1TH,
P235GH, P265GH, P295GH,
S235JRS1–S235J4S, S355G1S–S355G3S,
S255N–S355N, P255NH–P355NH,
S255NL–S355NL,
GE200–GE260, GE300
ASTM ve API çelikleri:
ASTM A27, A36 (tüm sınıflar), A214, A242 Gr.1–5,
A266 Gr.1, 2, 4, A283 Gr.A–D,
A285 Gr.A–C, A299 Gr.A–B, A328, A366,
A515 Gr.60–70, A516 Gr.55–70,
A570 Gr.30–45, A572 Gr.42–50,
A606 (tümü), A607 Gr.45, A656 Gr.50–60,
A668 Gr.A–B, A907 Gr.30–40, A841,
A851 Gr.1–2, A935 Gr.45, A936 Gr.50
API 5L Gr.B, X42, X52
BÖHLER Q E 7018 Kimyasal Analiz
|
Element |
Ağırlık % |
|
C |
0,07 |
|
Si |
0,5 |
|
Mn |
1,1 |
BÖHLER Q E 7018 Kaynak Metali Mekanik Özellikleri (Tipik / Minimum Değerler)
|
Durum |
Akma Day. Rp0,2 (MPa) |
Çekme Day. Rm (MPa) |
Uzama A % |
Darbe Enerjisi ISO-V (J) |
|
20°C / –20°C / –40°C |
||||
|
u |
490 (≥420) |
560 (500–640) |
27 (≥20) |
150 / 130 / ≥47 |
|
s |
430 |
520 |
29 |
170 / 150 / ≥47 |
u: Isıl işlem görmemiş, kaynaklı halde
s: Gerilim giderilmiş (600 °C / 2 saat, fırında 300 °C’ye kadar, sonra havada soğutma)
Çalışma Verileri
- Akım türü: DC (+)
|
Elektrot Çapı (mm) |
Akım (A) |
|
2.0 × 300 |
50 – 70 |
|
2.5 × 350 |
80 – 110 |
|
3.2 × 350 |
100 – 140 |
|
3.2 × 450 |
100 – 140 |
|
4.0 × 450 |
130 – 180 |
|
5.0 × 450 |
180 – 230 |
Elektrot tanımı:
Q E 7018 / 7018 / E 42 4 B
Yeniden Kurutma (Redrying)
300 – 350 °C / minimum 2 saat
Onaylar
- TÜV (19742.)
- DB (10.014.103)
- DNV
- CE
Genel Not
Bu bilgiler dikkatli inceleme ve kapsamlı araştırmalara dayanmaktadır.