Union AlMg 2,7 Mn 0,8
Solid wire for GTAW of AlMg alloys. The limited Mg-content of max. 2,8% to obtain intergranular corrosion resistance. Seawater resistant. Recommended for high-temperature applications. For obtaining near-matching coloured joints where anodizing is required.
| Normları: | EN ISO 18273 – S Al 5554 (AlMg2,7Mn) AWS A5.10 / SFA-5.10 – ER5554 |
||||||||||||
| Kaynak Metalinin Bileşimi % (Tipik) | Si | Mn | Ti | Fe | Cu | Al | Mg | Zn | Cr | Zr | V | Be | Diğer |
| < 0,25 | 0,5-0,8 | 0,05-0,15 | < 0,4 | bakiye | 2,4-2,8 | 0,05-0,2 | |||||||
| Mekanik Değerler: | Akma Dayanımı (MPa) | 90 | |||||||||||
| Çekme Dayanımı (MPa) | 200 | ||||||||||||
| Yüzde Uzama, A5,(%) | 17 | ||||||||||||
| Çentik Darbe Dayanımı (j/cm2 ) |
|||||||||||||
İlgili ürünler
Union AlCu 6 Mn
Solid wire for GMAW of AlCu alloys. Provides higher strength and better ductility than AlSi filler alloys when welding AlCu alloys. Superior resistance to stress corrosion cracking where high-temperature properties are required. Thorough cleaning of the workpiece bevels is necessary prior to welding.
Union AlSi 10 Cu 4
Solid wire for GMAW of AlCu alloys. Low melting point and excellent penetration characteristics. Provides superior wetting characteristics compared to Union AlCu 6 Mn when welding AlCu alloys, the strength, on the other hand, is lower. Superior resistance to stress corrosion cracking where high-temperature properties are required. The weld metal is not suitable for anodizing for decorative purposes. Thorough cleaning of the workpiece bevels is necessary prior to welding.
UTP 48
UTP 48 contains 12% Si for welding of aluminium alloyed with copper, silicon, and magnesium. Also excellent for joining dissimilar grades of aluminium. Unique self-lifting slag. Pure white coating outlasts conventional products in moisture resistance. Available in hermetically sealed aluminium tins.
UTP 485
UTP 485 is an aluminium stick electrode with 5% Si and a special coating. It is suitable for joining and surfacing AlSi alloys with a Si content of up to 7% and for dissimilar joints of different Al-alloys, such as:
3.3206 AlMgSi 0.5 - 3.2371 G-AlSi 7 Mg
3.3210 AlMgSi 0.7 - 3.2341 G-AlSi 5 Mg
3.2315 AlMgSi 1 - 3.2151 G-AlSi 6 Cu 4
3.3211 AlMg 1 SiCu
UTP 485 is suitable for welding plates of wall thicknesses> 2 mm. The soft arc produces a fl at, fi newly-rippled weld seam. Easy slag removal.
UTP 49
UTP 49 for welding of aluminium alloyed with manganese and magnesium. Also excellent for joining dissimilar grades of aluminium. Suitable for seawater applications. Unique self-lifting slag. Pure white coating outlasts conventional products in moisture resistance. Available in hermetically sealed aluminium tins.