Union AlMg 4,5 Mn Zr
Zirconium micro-alloyed aluminium wire. The weld metal is uncritical in terms of hot cracks. Suitable especially for complicated welding constructions with critical tensions. Base material
should be cleaned near the seam. Pre-heating 150°C for plates > 15 mm.
| Normları: | EN ISO 18273 – S Al 5087 (AlMg4,5MnZr AWS A5.10 / SFA-5.10 – ER5087 |
||||||||||||
| Kaynak Metalinin Bileşimi % (Tipik) | Si | Mn | Ti | Fe | Cu | Al | Mg | Zn | Cr | Zr | V | Be | Diğer |
| < 0,25 | 0,75-1,0 | < 0,15 | bakiye | 4,5-5,2 | < 0,25 | 0,05-0,25 | 0,1-0,2 | ||||||
| Mekanik Değerler: | Akma Dayanımı (MPa) | 125 | |||||||||||
| Çekme Dayanımı (MPa) | 275 | ||||||||||||
| Yüzde Uzama, A5,(%) | 16 | ||||||||||||
| Çentik Darbe Dayanımı (j/cm2 ) |
|||||||||||||
İlgili ürünler
Union AlSi 5
Rods for GTAW of AlSi containing up to 5% Si. Oxyacetylene welding respectively brazing with suitable fl uxes possible. The weld metal is not suitable for anodizing for decorative purposes. Very fl uid weld pool. Base material should be cleaned near the seam. Pre-heating 150 - 200°C for plates > 15 mm. Do not use for welding hardenable alloys is highly stressed zones.
Union AlSi 7 Mg
Union AlSi 7 Mg is a modified 4010 alloy (alloy 4008) with low levels of impurities, specially designed for joining or repairing 7% Si aluminium cast components like 356.0, A356.0 and A357.0. The mechanical properties can be increased by heat treatment. Thorough cleaning of the workpiece bevels is necessary prior to welding.
UTP 485
UTP 485 is an aluminium stick electrode with 5% Si and a special coating. It is suitable for joining and surfacing AlSi alloys with a Si content of up to 7% and for dissimilar joints of different Al-alloys, such as:
3.3206 AlMgSi 0.5 - 3.2371 G-AlSi 7 Mg
3.3210 AlMgSi 0.7 - 3.2341 G-AlSi 5 Mg
3.2315 AlMgSi 1 - 3.2151 G-AlSi 6 Cu 4
3.3211 AlMg 1 SiCu
UTP 485 is suitable for welding plates of wall thicknesses> 2 mm. The soft arc produces a fl at, fi newly-rippled weld seam. Easy slag removal.