UTP 49 for welding of aluminium alloyed with manganese and magnesium. Also excellent for joining dissimilar grades of aluminium. Suitable for seawater applications. Unique self-lifting slag. Pure white coating outlasts conventional products in moisture resistance. Available in hermetically sealed aluminium tins.

Add to wishlist
Kategoriler:
Açıklama
Normları: EN ISO 18273 –  E Al 3103 (AlMn1)
AWS A5.3 / SFA-5.3 –  E3003
Kaynak Metalinin Bileşimi % (Tipik) Si Mn Ti Fe Cu Al Mg Zn Cr Zr V Be Diğer
0,4 1,3 0,3 bakiye
Mekanik Değerler: Akma Dayanımı (MPa) 40
Çekme Dayanımı (MPa) 110
Yüzde Uzama, A5,(%) 20
Çentik Darbe Dayanımı (j/cm2
)
Diğer Bilgiler

Değerlendirmeler

Henüz değerlendirme yapılmadı.

“UTP 49” için yorum yapan ilk kişi siz olun

E-posta adresiniz yayınlanmayacak. Gerekli alanlar * ile işaretlenmişlerdir

İlgili ürünler

Union AlMg 4,5 Mn

TIG-rod for welding of AlMg alloys. The weld metal is resistant to seawater. Base material should be cleaned near the seam. Pre-heating 150°C for plates > 15 mm.
Add to wishlist
Quick view

Union AlMg 3

Solid wire for AlMg alloys containing up to 3% Mg. Seawater-resistant weld metal. Good colour matching with base metal after anodizing. Thorough cleaning of the workpiece bevels is necessary. Thicker plate materials require preheating to 150°C.
Add to wishlist
Quick view

Union AlSi 12

Is used for aluminium-silicium casting alloy with a Si-content up to 12%. Good mechanical characteristics, excellent corrosion resistance and a low melting point ensure high-quality welding results.
Add to wishlist
Quick view

Union AlMg 4,5 Mn

Solid wire for GMAW and GTAW of AlMg alloys. The weld metal is resistant to seawater. Base material should be cleaned near the seam. Pre-heating 150°C for plates > 15 mm.
Add to wishlist
Quick view

Union AlSi 5

Rods for GTAW of AlSi containing up to 5% Si. Oxyacetylene welding respectively brazing with suitable fl uxes possible. The weld metal is not suitable for anodizing for decorative purposes. Very fl uid weld pool. Base material should be cleaned near the seam. Pre-heating 150 - 200°C for plates > 15 mm. Do not use for welding hardenable alloys is highly stressed zones.
Add to wishlist
Quick view

Union AlMg 5

Solid wire for AlMg alloys containing up to 5% Mg. Seawater-resistant weld metal. Good colour matching with base metal after anodizing. Thorough cleaning of the workpiece bevels is necessary. Thicker plate materials require preheating to 150°C.
Add to wishlist
Quick view

Union 99,5 Ti (TIG)

Pure aluminium welding rod for joining and surfacing of aluminium with a maximum of 0.5% of alloyed elements. The welding consumable contains Ti for grain refinery. Base material should be cleaned near the seam.
Add to wishlist
Quick view

Union AlCu 6 Mn

Solid wire for GMAW of AlCu alloys. Provides higher strength and better ductility than AlSi filler alloys when welding AlCu alloys. Superior resistance to stress corrosion cracking where high-temperature properties are required. Thorough cleaning of the workpiece bevels is necessary prior to welding.
Add to wishlist
Quick view