Union AlCu 6 Mn

Solid wire for GMAW of AlCu alloys. Provides higher strength and better ductility than AlSi filler alloys when welding AlCu alloys. Superior resistance to stress corrosion cracking where high-temperature properties are required. Thorough cleaning of the workpiece bevels is necessary prior to welding.

Add to wishlist
Kategoriler:
Açıklama
Normları: EN ISO 18273 – S Al 2319 (AlCu6MnZrTi)
AWS A5.10 / SFA-5.10 – ER2319
Kaynak Metalinin Bileşimi % (Tipik) Si Mn Ti Fe Cu Al Mg Zn Cr Zr V Be Diğer
0,2-0,4 0,1-0,2 5,8-6,8 bakiye < 0,02 0,10-0,25 0,05-0,15
Mekanik Değerler: Akma Dayanımı (MPa) 150
Çekme Dayanımı (MPa) 250
Yüzde Uzama, A5,(%) 12
Çentik Darbe Dayanımı (j/cm2)
Diğer Bilgiler

Değerlendirmeler

Henüz değerlendirme yapılmadı.

“Union AlCu 6 Mn” için yorum yapan ilk kişi siz olun

E-posta adresiniz yayınlanmayacak. Gerekli alanlar * ile işaretlenmişlerdir

İlgili ürünler

Union AlMg 4,5 Mn Zr

Zirconium micro-alloyed aluminium TIG rod. The weld metal is uncritical in terms of hot cracks. Suitable especially for complicated welding constructions with critical tensions. Base material should be cleaned near the seam. Pre-heating 150°C for plates > 15 mm.
Add to wishlist
Quick view

Union AlMg 4,5 Mn Zr

Zirconium micro-alloyed aluminium wire. The weld metal is uncritical in terms of hot cracks. Suitable especially for complicated welding constructions with critical tensions. Base material should be cleaned near the seam. Pre-heating 150°C for plates > 15 mm.
Add to wishlist
Quick view

Union AlMg 3

Solid wire for AlMg alloys containing up to 3% Mg. Seawater-resistant weld metal. Good colour matching with base metal after anodizing. Thorough cleaning of the workpiece bevels is necessary. Thicker plate materials require preheating to 150°C.
Add to wishlist
Quick view

Union AlSi 5

Rods for GTAW of AlSi containing up to 5% Si. Oxyacetylene welding respectively brazing with suitable fl uxes possible. The weld metal is not suitable for anodizing for decorative purposes. Very fl uid weld pool. Base material should be cleaned near the seam. Pre-heating 150 - 200°C for plates > 15 mm. Do not use for welding hardenable alloys is highly stressed zones.
Add to wishlist
Quick view

Union AlMg 4,5 Mn

TIG-rod for welding of AlMg alloys. The weld metal is resistant to seawater. Base material should be cleaned near the seam. Pre-heating 150°C for plates > 15 mm.
Add to wishlist
Quick view

Union 99,5 Ti (solid)

Is a pure aluminium welding wire for joining and surfacing of aluminium materials according to EN ISO 18273. It is a welding consumable with Ti for grain refinement and weldable in all positions.
Add to wishlist
Quick view

Union AlSi 10 Cu 4

Solid wire for GMAW of AlCu alloys. Low melting point and excellent penetration characteristics. Provides superior wetting characteristics compared to Union AlCu 6 Mn when welding AlCu alloys, the strength, on the other hand, is lower. Superior resistance to stress corrosion cracking where high-temperature properties are required. The weld metal is not suitable for anodizing for decorative purposes. Thorough cleaning of the workpiece bevels is necessary prior to welding.
Add to wishlist
Quick view

Union AlSi 10 Cu 4

Rod for GTAW of AlCu alloys. Low melting point and excellent penetration characteristics. Provides superior wetting characteristics compared to Union AlCu 6 Mn when welding AlCu alloys, the strength, on the other hand, is lower. Superior resistance to stress corrosion cracking where high-temperature properties are required. The weld metal is not suitable for anodizing for decorative purposes. Thorough cleaning of the workpiece bevels is necessary prior to welding.
Add to wishlist
Quick view