Union AlMg 5 Mn Ti

Solid wire for GMAW of AlMg alloys containing up to 5% Mg. Seawater-resistant weld metal. Susceptible to stress corrosion cracking if exposed to service temperatures > 65°C. Good colour matching with base metal after anodizing. The welding consumable contains Ti for grain refinery. Thorough cleaning of the workpiece bevels is necessary prior to welding.

Add to wishlist
Kategoriler:
Açıklama
Normları: EN ISO 18273 – S Al 5556 (AlMg5Mn1Ti(A))
AWS A5.10 / SFA-5.10 – ER5556
Kaynak Metalinin Bileşimi % (Tipik) Si Mn Ti Fe Cu Al Mg Zn Cr Zr V Be Diğer
0,5-1,0 0,05-0,20 < 0,4 bakiye 4,7-5,5 < 0,25 0,05-0,20
Mekanik Değerler: Akma Dayanımı (MPa) 125
Çekme Dayanımı (MPa) 275
Yüzde Uzama, A5,(%) 17
Çentik Darbe Dayanımı (j/cm2
)
Diğer Bilgiler

Değerlendirmeler

Henüz değerlendirme yapılmadı.

“Union AlMg 5 Mn Ti” için yorum yapan ilk kişi siz olun

E-posta adresiniz yayınlanmayacak. Gerekli alanlar * ile işaretlenmişlerdir

İlgili ürünler

Union AlMg 4,5 Mn

TIG-rod for welding of AlMg alloys. The weld metal is resistant to seawater. Base material should be cleaned near the seam. Pre-heating 150°C for plates > 15 mm.
Add to wishlist
Quick view

Union AlMg 2,7 Mn 0,8

Rods for GTAW of AlMg alloys. Mg-content max. 2,8% to obtain intergranular corrosion resistance. Seawater-resistant weld metal. For obtaining near-matching coloured joints where anodizing is required. Pre-heating 150°C for plates > 15 mm.
Add to wishlist
Quick view

Union Al 99,7

Aluminium solid wire rod for welding of very pure aluminium materials according to EN ISO 18273 for applications in electro technical and mechanical construction, food, and chemical industry.
Add to wishlist
Quick view

Union AlCu 6 Mn

Solid wire for GMAW of AlCu alloys. Provides higher strength and better ductility than AlSi filler alloys when welding AlCu alloys. Superior resistance to stress corrosion cracking where high-temperature properties are required. Thorough cleaning of the workpiece bevels is necessary prior to welding.
Add to wishlist
Quick view

Union AlMg 3

Solid wire for AlMg alloys containing up to 3% Mg. Seawater-resistant weld metal. Good colour matching with base metal after anodizing. Thorough cleaning of the workpiece bevels is necessary. Thicker plate materials require preheating to 150°C.
Add to wishlist
Quick view

Union AlSi 12

Rods for GTAW of AlSi containing more than 10% Si. Very fluid weld pool. The weld metal is not suitable for anodizing. Pre-heating 150 – 200°C for plates > 15 mm.
Add to wishlist
Quick view

Union Al 99,7

Aluminium solid wire for welding of very pure aluminium materials according to EN ISO 18273 for applications in electro technical and mechanical construction, food and chemical industry.
Add to wishlist
Quick view

Union AlMg 5 Mn Ti

Rod for GTAW of AlMg alloys containing up to 5% Mg. Seawater-resistant weld metal. Susceptible to stress corrosion cracking if exposed to service temperatures >65°C. Good colour matching with base metal after anodizing. The welding consumable contains Ti for grain refinery. Thorough cleaning of the workpiece bevels is necessary prior to welding.
Add to wishlist
Quick view