| Normları: | EN ISO 18273 – S Al 4018 (AlSi7Mg) AWS A5.10 / SFA-5.10 – ER4018 |
||||||||||||
| Kaynak Metalinin Bileşimi % (Tipik) | Si | Mn | Ti | Fe | Cu | Al | Mg | Zn | Cr | Zr | V | Be | Diğer |
| 6,5-7,5 | < 0,05 | 0,04-0,15 | < 0,1 | < 0,05 | bakiye | 0,5-0,8 | |||||||
| Mekanik Değerler: | Akma Dayanımı (MPa) | 55 | |||||||||||
| Çekme Dayanımı (MPa) | 165 | ||||||||||||
| Yüzde Uzama, A5,(%) | 18 | ||||||||||||
| Çentik Darbe Dayanımı (j/cm2 ) |
|||||||||||||
Union AlSi 7 Mg
Union AlSi 7 Mg is a modified 4010 alloy (alloy 4008) with low levels of impurities, specially designed for joining or repairing 7% Si aluminium cast components like 356.0, A356.0 and A357.0. The mechanical properties can be increased by heat treatment. Thorough cleaning of the workpiece bevels is necessary prior to welding.
Açıklama
Diğer Bilgiler
İlgili ürünler
Union AlMg 5 Mn (solid)
Solid wire for GMAW of AlMg alloys containing up to 5% Mg. Seawater-resistant weld metal. Susceptible to stress corrosion cracking if exposed to service temperatures > 65°C. Good colour matching with base metal after anodizing. Thorough cleaning of the workpiece bevels is necessary prior to welding.
Union AlMg 5 Mn Ti
Rod for GTAW of AlMg alloys containing up to 5% Mg. Seawater-resistant weld metal. Susceptible to stress corrosion cracking if exposed to service temperatures >65°C. Good colour matching with base metal after anodizing. The welding consumable contains Ti for grain refinery. Thorough cleaning of the workpiece bevels is necessary prior to welding.
Union AlSi 10 Cu 4
Solid wire for GMAW of AlCu alloys. Low melting point and excellent penetration characteristics. Provides superior wetting characteristics compared to Union AlCu 6 Mn when welding AlCu alloys, the strength, on the other hand, is lower. Superior resistance to stress corrosion cracking where high-temperature properties are required. The weld metal is not suitable for anodizing for decorative purposes. Thorough cleaning of the workpiece bevels is necessary prior to welding.
Union AlSi 10 Cu 4
Rod for GTAW of AlCu alloys. Low melting point and excellent penetration characteristics. Provides superior wetting characteristics compared to Union AlCu 6 Mn when welding AlCu alloys, the strength, on the other hand, is lower. Superior resistance to stress corrosion cracking where high-temperature properties are required. The weld metal is not suitable for anodizing for decorative purposes. Thorough cleaning of the workpiece bevels is necessary prior to welding.