| Normları: | EN ISO 18273 – S Al 5754 (AlMg3) AWS A5.10 / SFA-5.10 – ER5754(mod.) |
||||||||||||
| Kaynak Metalinin Bileşimi % (Tipik) | Si | Mn | Ti | Fe | Cu | Al | Mg | Zn | Cr | Zr | V | Be | Diğer |
| 0,1-0,6 | < 0,15 | bakiye | 2,6-3,6 | < 0,3 | |||||||||
| Mekanik Değerler: | Akma Dayanımı (MPa) | 80 | |||||||||||
| Çekme Dayanımı (MPa) | 180 | ||||||||||||
| Yüzde Uzama, A5,(%) | 18 | ||||||||||||
| Çentik Darbe Dayanımı (j/cm2 ) |
|||||||||||||
Union AlMg 3
Rods for GTAW of AlMg containing up to 3% Mg. Seawater-resistant weld metal. Good colour matching with base metal after anodizing. Base material should be cleaned near the seam. Pre-heating 150°C for plates > 15 mm.
Açıklama
Diğer Bilgiler
İlgili ürünler
Union AlCu 6 Mn
Solid wire for GMAW of AlCu alloys. Provides higher strength and better ductility than AlSi filler alloys when welding AlCu alloys. Superior resistance to stress corrosion cracking where high-temperature properties are required. Thorough cleaning of the workpiece bevels is necessary prior to welding.
Union AlSi 5
Rods for GTAW of AlSi containing up to 5% Si. Oxyacetylene welding respectively brazing with suitable fl uxes possible. The weld metal is not suitable for anodizing for decorative purposes. Very fl uid weld pool. Base material should be cleaned near the seam. Pre-heating 150 - 200°C for plates > 15 mm. Do not use for welding hardenable alloys is highly stressed zones.