| Normları: | EN ISO 18273 – S Al 5183 (AlMg 4,5Mn0,7(A)) AWS A5.10 / SFA-5.10 – ER5183 |
||||||||||||
| Kaynak Metalinin Bileşimi % (Tipik) | Si | Mn | Ti | Fe | Cu | Al | Mg | Zn | Cr | Zr | V | Be | Diğer |
| 0,5-1,0 | < 0,15 | bakiye | 4,3-5,2 | 0,05-0,25 | |||||||||
| Mekanik Değerler: | Akma Dayanımı (MPa) | 125 | |||||||||||
| Çekme Dayanımı (MPa) | 275 | ||||||||||||
| Yüzde Uzama, A5,(%) | 17 | ||||||||||||
| Çentik Darbe Dayanımı (j/cm2 ) |
|||||||||||||
Union AlMg 4,5 Mn
Solid wire for GMAW and GTAW of AlMg alloys. The weld metal is resistant to seawater. Base material should be cleaned near the seam. Pre-heating 150°C for plates > 15 mm.
Açıklama
Diğer Bilgiler
İlgili ürünler
Union AlMg 5 Mn Ti
Rod for GTAW of AlMg alloys containing up to 5% Mg. Seawater-resistant weld metal. Susceptible to stress corrosion cracking if exposed to service temperatures >65°C. Good colour matching with base metal after anodizing. The welding consumable contains Ti for grain refinery. Thorough cleaning of the workpiece bevels is necessary prior to welding.
Union AlSi 5
Rods for GTAW of AlSi containing up to 5% Si. Oxyacetylene welding respectively brazing with suitable fl uxes possible. The weld metal is not suitable for anodizing for decorative purposes. Very fl uid weld pool. Base material should be cleaned near the seam. Pre-heating 150 - 200°C for plates > 15 mm. Do not use for welding hardenable alloys is highly stressed zones.
Union AlSi 10 Cu 4
Solid wire for GMAW of AlCu alloys. Low melting point and excellent penetration characteristics. Provides superior wetting characteristics compared to Union AlCu 6 Mn when welding AlCu alloys, the strength, on the other hand, is lower. Superior resistance to stress corrosion cracking where high-temperature properties are required. The weld metal is not suitable for anodizing for decorative purposes. Thorough cleaning of the workpiece bevels is necessary prior to welding.