BÖHLER CM 9-IG

Class

%5 Cr – %0,5 Mo alaşımlı çelikler ve özellikle in oil refineries kullanılan in hot hydrogen service için uygun bir GMAW (MIG/MAG) wire. Özellikle X12CrMo5 Weight % P5 gibi çelik kalitelerinde, up to +650 °C olan servis sıcaklıklarında tercih edilir.

The wire exhibits excellent wire feeding characteristics, which ensure smooth welding and a fluid weld pool. It has a homogeneous copper coating with a low total copper content.

cast steels

Yüksek sıcaklık çelikleri ve benzer alaşımlı döküm çelikler,
benzer alaşımlı ve up to 1180 MPa QT-çelikler

• 1.7362 – X12CrMo5

is a basic-coated, core-wired alloyed covered electrode designed for shielded metal arc welding (SMAW). The 9Cr-1Mo weld metal exhibits a fully tempered martensitic microstructure with suitable mechanical properties after post-weld heat treatment.

• A 182 Gr. F5
• A 193 Gr. B5
• A 213 Gr. T5
• A 217 Gr. C5
• A 234 Gr. WP5
• A 314 Gr. 501
• A 335 Gr. P5 and P5c
• A 369 Gr. FB 5
• A 387 Grade 5
• A 426 Gr. CP5

Typical Chemical Analysis of Solid Wire (% by weight)

Mechanical Properties of the Base Metal

Status:
a – Tavlanmış (730 °C / 2 saat / fırında 300 °C’ye kadar soğutma / hava)
Koruyucu gaz: Ar + %18 CO₂

Job Information

• Current Type / Polarity: DC (+)
• Gas flow rate: Argon + 15–25% CO₂
• Wire diameter: Ø 1.2 mm

en az 150°C paso arası sıcaklık

• Preheating and interpass temperature: 150–300 °C
• Iridescence: Legal Notice, at least 1 hour
• Soğutma: Fırında up to 300 °C, ardından durgun hava

Note

Verilen tüm bilgiler dikkatli inceleme ve yoğun araştırmalara dayanmaktadır.
Bununla birlikte, doğruluk konusunda herhangi bir sorumluluk kabul edilmez ve bilgiler önceden haber verilmeksizin değiştirilebilir.