Böhler Diamondspark X80 RC-Pipe

cast steels

Similar alloyed, wear-resistant steels:

• 1.4903 – X10CrMoVNb9-1
• GX12CrMoVNbN9-1

Metal-core wire, high-alloy, creep-resistant

• ASTM A 335 Gr. P91
• ASTM A 336 Gr. F91
• ASTM A 369 Gr. FP91
• ASTM A 387 Gr. 91
• ASTM A 213 Gr. T91

Böhler FOXcore C 9 MV MC Chemical Analyzer

Mechanical Properties of Böhler FOXcore C 9 MV MC Weld Metal

(Typical values / minimum values)**

s – After voltage relief:
760 °C / 3 saat, fırında 300 °C’ye kadar soğutma, ardından havada soğutma
Protective gas: Argon + %2,5 CO₂

s – Gerilim giderme sonrası:

• Current Type / Polarity: DC+
• Wire diameter: 1.2 mm
• Shielding gas (EN ISO 14175): Ar + 2.5% CO₂

artık gerilmeler

• Welding can be done with conventional or pulsed power supplies.
• Tercihen slightly rearward positioning of the torch, with of approximately 80° torch angle önerilir.
• 80° torç açısı 18 – 20 mm
• Arc length: 3 – 5 mm

Preheating and interpass temperature: below 100 °C
Kaynak sonrası, martenzitik dönüşümün tamamlanabilmesi için kaynaklı birleşim below 80 °C soğutulmalıdır.

Kalın cidarlı veya karmaşık parçalarda residual stresses This should be taken into account.

Post-Weld Heat Treatment (PWHT) – Recommended

• Annealing: 760 °C
• Duration: en az 2 saat, en fazla 10 saat
• maks. 150 °C/saat
  • Above 550 °C: max. 150 °C/hour
  • 80 °C/hour max. 80 °C/hour

Position Resource Capability

Metal özlü tellerin pozisyon kaynağı kabiliyeti, It is similar to solid wires..

Approvals

• —

Note

Bu belgede verilen tüm bilgiler dikkatli inceleme ve kapsamlı araştırmalara dayanmaktadır.
Ancak doğruluk konusunda herhangi bir sorumluluk kabul edilmez ve bilgiler is subject to change without prior notice.